Induction Hardening Chain Process

Objective Induction Hardening chain at a rate of 0.16″ – 26″ (4 mm – 0.66 m) per minute at 1580˚F (860˚C) then tempering at a rate of 0.31″ – 36″ (8 mm – 0.92 M) per minute at 400˚F (204˚C), for an overall productivity rate of hardening 0.16″ – 26 lbs (4 mm – 12 kg) per hour and tempering 0.31″ – 163 lbs (8 mm – 74 kg) per hour. Recommended Equipment The recommended equipment for this application is the DW-UHF-10KW induction heating machine

Material to be heated: Alloy Steel Chain 0.12″ to 0.31″ (3 mm to 8 mm) Weight: 0.77 lb – 4 lbs (0.35 kg – 2 kg) per meter Key Parameters Hardness: 47 – 48 HRC Power: 10 kW Temperature: Hardening- 1580˚F (860˚C) Tempering- 204˚F (400˚C) Time: Hardening- 0.16″ – 26″ (4 mm – 0.66 M) per minute Tempering- 0.31″ – 36″ (8 mm – 0.92 M) per minute