Induction Brazing Carbide to Steel

Objective High frequency induction brazing carbide to steel. Recommended Equipment The recommended equipment for this application is the DW-HF-45KW induction brazing machine with the remote heating station.
induction brazing machineMaterials:
  • Large magnetic steel drill head with carbides. Head is approx. 8” OD x 4” (203.2mm OD x 101.6mm) thick, shaft is 11” (279.4mm) long x 2”(50.8mm) to 5” (127mm) OD.
  • Carbides 1.125” (28.5mm) long x 0.75”(19.05mm) OD with dome shaped top attached to the head, recessed approx. 0.8” (20.3mm) into the head.
Power: Up to 37kW Temperature: 1500°F  + (815°C+) Time: Alloy flows at the outer most carbides in 50 seconds.  The center and inner carbides start to show alloy dripping at 1 minute and 40 seconds.
Results and Conclusions: Tests results show that carbide removal is possible.  Initially, the part needs to be heated and held at temperature to allow the induction brazing alloy to drip out.  It is important to fixture the part with carbides facing down.  An external shock is needed afterwards to shift the carbides out enough to allow them to be grabbed with a set of pliers. Caution: when pulling out the carbides, hot molten induction brazing alloy can flow out of the holes for the carbides when they are pulled out.
https://dw-inductionheater.com/induction-brazing-carbide-to-steelbrazing-tungsten-carbide-to-stainless-steel.html?feed_id=237324&_unique_id=65f8e6a800a0b

关注者

博客归档

我的简介

我的照片
HLQ induction heating machine manufacturer provides the service of induction brazing,melting,hot forming,hardening surface,annealing,shrink fitting,PWHT,etc.