induction Brazing copper rods to brass strips

Objective Induction Brazing copper rods to brass strips to replace torch operation. The current torch process results in excessive contaminants on the assembly, and requires extensive rework after the induction brazing operation.
Equipment DW-UHF-10KW INDUCTION BRAZING MACHINE Two turn open end conveyor coil Materials • Copper coupon plate and copper rod • Braze wire – EZ Flo 45 • Braze alloy – 45% Silver, 1/32 DIA
Key Parameters – TEST 1 Power: 7.2 kW Temperature: Approximately 1350° F (732° C) Time: Average time – 100 seconds Process and Results: For Induction brazing copper plate to copper rod,, EZ Flo 45 braze wire was cut into 2” lengths and placed in the interface area. In a production situation, EZ Flo 45 brazing paste is recommended. The assemblies were set up and heated for an average time of 100 seconds to flow the alloy and achieve the braze.
Key Parameters – TEST 1 Power: 6 kW Temperature: Approximately 1350° F (732° C) Time: Average time – 2.5 minutes Process and Results: For Induction brazing copper rod to brass plate,, EZ Flo 45 braze wire was cut into 2” lengths and placed in the interface area. In a production situation, EZ Flo 45 brazing paste is recommended. The assemblies were set up (see photographs) and heated for an average time of 2.5 minutes to flow the alloy and achieve the braze. Due to the metal resistance differential between copper and brass, the brass bar heat preferentially. The induction heating coil designed to braze the bars to the plate section heats the rods and the heat is transferred to the plate more by conduction than induction causing the bars to initially reach temperature prior to the plate. If the materials are the same (cooper to copper or brass to brass, this is not a problem. If the bar is copper and the plate is brass there are not issues – only when the bar is brass and the plate is copper. This requires the power to be reduced to allow tie for heat transfer from the brass rod to the copper plate.
Key Parameters – TEST 1 Power: 7.2 kW Temperature: Approximately 1350° F (732° C) Time: Average time – 2 minutes Process and Results: For Induction braze copper coupon plate and copper rod,, EZ Flo 45 braze wire was cut into 2” lengths and placed in the interface area. In a production situation, EZ Flo 45 brazing paste is recommended. The assemblies were set up  and heated for an average time of 2 minutes to flow the alloy and achieve the braze.
Results/Benefits:
  • induction brazing Strong durable joints
  • Selective and precise heat zone, resulting in less part distortion and joint stress than welding
  • Less oxidation
  • Faster heating cycles
  • More consistent results and suitability for large volume production, without the need for batch processing
  • Safer than flame brazing