induction heating hot rolling with IGBT induction heating system
Objective To heat the circumference of plough discs before hot rolling (sharpening) process
Material Flat Boron steel discs, OD 460 to 710 mm (18 to 28”) thickness 3.2 to 10 mm (8/64 to 25/64”)
Temperature 725°C 1335°F
Frequency 75 kHz
Equipment DW-HF-120 kW induction heating system using 2 work heads, switching system, 4 specially-designed coils, chiller system
Process In a PLC system, each of two rolling machines is equipped with a remote work head and with a rotating platform where the disc is held horizontally and held in position by a central nonmagnetic
plate 100 mm less that the disc diameter. The 250 mm (10”) heating coil is positioned over the blade, rotationally ahead of pressure rolls. This heats the entire edge of the disc.
After a few seconds of heating, the edge reaches the required temperature and the disc is made to turn at 30 rpm. The pressure rolls close, forming the sharp edge profile. The final edge is obtained after two turns of the disc.
Results/Benefits Induction heating provides a much more rapid process compared to cold-rolling; the desired profile is achieved after a few seconds, compared with a few minutes. The metallurgical quality of the finished edge is higher, since the process effectively hardens the material.
The equipment and process lend themselves to robotic automation
https://dw-inductionheater.com/wp-content/uploads/2015/04/induction-heating-hot-rolling.jpg
https://dw-inductionheater.com/induction-heating-hot-rolling.html
heating hot rolling, high frequency hot rolling, hot rolling, hot rolling induction, hot rolling machine, induction heating hot rolling, induction hot rolling, RF heating hot rolling