High frequency magnetic induction brazing stainless steel to steel process
HLQ team was provided with 2 different parts to be brazed in our test laboratory.
Objective: Induction Brazing of a 0.15’’/ 3.81mm stainless steel pin to a steel base.
Equipment: DW-UHF-6KW-III handheld induction brazing system
Industry: Appliances & HVAC
Materials:
Steel hexagon (base 1’’/ 25.4 mm diameter; 0.1’’/ 2.54 mm wall thickness)
A stainless steel pin (0.15’’/ 3.81 mm)
Other Materials:
All-purpose black brazing flux
Power: 1.43 kW
Temperature: 1400 °F/ 760°C
Time: 8 seconds
Process:
The two workpieces were carefully positioned together. All-purpose
induction brazing black flux was added because it is ideal for high-temperature applications where rapid, localized heating is needed. The process of
induction brazing was performed successfully within 8 seconds by using the
DW-UHF-6KW-III handheld induction brazing system, producing the
induction heating power of 1.43 kW at 1400 °F/ 760°C.