induction brazing stainless steel to steel

High frequency magnetic induction brazing stainless steel to steel process

HLQ team was provided with 2 different parts to be brazed in our test laboratory. Objective: Induction Brazing of a 0.15’’/ 3.81mm stainless steel pin to a steel base. Equipment:  DW-UHF-6KW-III handheld induction brazing system  Industry: Appliances & HVAC Materials: Steel hexagon (base 1’’/ 25.4 mm diameter; 0.1’’/ 2.54 mm wall thickness) A stainless steel pin (0.15’’/ 3.81 mm) Other Materials:  All-purpose black brazing flux Power: 1.43 kW Temperature: 1400 °F/ 760°C Time: 8 seconds Process: The two workpieces were carefully positioned together. All-purpose induction brazing black flux was added because it is ideal for high-temperature applications where rapid, localized heating is needed. The process of induction brazing was performed successfully within 8 seconds by using the  DW-UHF-6KW-III handheld induction brazing system, producing the induction heating power of 1.43 kW at 1400 °F/ 760°C. https://dw-inductionheater.com/high-frequency-magnetic-induction-brazing-stainless-steel-to-steel-process.html?feed_id=238194&_unique_id=66000a7b141d8

induction brazing stainless steel to steel

High frequency magnetic induction brazing stainless steel to steel process

HLQ team was provided with 2 different parts to be brazed in our test laboratory. Objective: Induction Brazing of a 0.15’’/ 3.81mm stainless steel pin to a steel base. Equipment:  DW-UHF-6KW-III handheld induction brazing system  Industry: Appliances & HVAC Materials: Steel hexagon (base 1’’/ 25.4 mm diameter; 0.1’’/ 2.54 mm wall thickness) A stainless steel pin (0.15’’/ 3.81 mm) Other Materials:  All-purpose black brazing flux Power: 1.43 kW Temperature: 1400 °F/ 760°C Time: 8 seconds Process: The two workpieces were carefully positioned together. All-purpose induction brazing black flux was added because it is ideal for high-temperature applications where rapid, localized heating is needed. The process of induction brazing was performed successfully within 8 seconds by using the  DW-UHF-6KW-III handheld induction brazing system, producing the induction heating power of 1.43 kW at 1400 °F/ 760°C.

induction brazing stainless steel to steel

High frequency magnetic induction brazing stainless steel to steel process

HLQ team was provided with 2 different parts to be brazed in our test laboratory. Objective: Induction Brazing of a 0.15’’/ 3.81mm stainless steel pin to a steel base. Equipment:  DW-UHF-6KW-III handheld induction brazing system  Industry: Appliances & HVAC Materials: Steel hexagon (base 1’’/ 25.4 mm diameter; 0.1’’/ 2.54 mm wall thickness) A stainless steel pin (0.15’’/ 3.81 mm) Other Materials:  All-purpose black brazing flux Power: 1.43 kW Temperature: 1400 °F/ 760°C Time: 8 seconds Process: The two workpieces were carefully positioned together. All-purpose induction brazing black flux was added because it is ideal for high-temperature applications where rapid, localized heating is needed. The process of induction brazing was performed successfully within 8 seconds by using the  DW-UHF-6KW-III handheld induction brazing system, producing the induction heating power of 1.43 kW at 1400 °F/ 760°C. https://dw-inductionheater.com/high-frequency-magnetic-induction-brazing-stainless-steel-to-steel-process.html?feed_id=221386&_unique_id=64c899b3307e9

induction brazing stainless steel to steel

High frequency magnetic induction brazing stainless steel to steel process

HLQ team was provided with 2 different parts to be brazed in our test laboratory. Objective: Induction Brazing of a 0.15’’/ 3.81mm stainless steel pin to a steel base. Equipment:  DW-UHF-6KW-III handheld induction brazing system  Industry: Appliances & HVAC Materials: Steel hexagon (base 1’’/ 25.4 mm diameter; 0.1’’/ 2.54 mm wall thickness) A stainless steel pin (0.15’’/ 3.81 mm) Other Materials:  All-purpose black brazing flux Power: 1.43 kW Temperature: 1400 °F/ 760°C Time: 8 seconds Process: The two workpieces were carefully positioned together. All-purpose induction brazing black flux was added because it is ideal for high-temperature applications where rapid, localized heating is needed. The process of induction brazing was performed successfully within 8 seconds by using the  DW-UHF-6KW-III handheld induction brazing system, producing the induction heating power of 1.43 kW at 1400 °F/ 760°C.

induction brazing stainless steel to steel

High frequency magnetic induction brazing stainless steel to steel process

HLQ team was provided with 2 different parts to be brazed in our test laboratory. Objective: Induction Brazing of a 0.15’’/ 3.81mm stainless steel pin to a steel base. Equipment:  DW-UHF-6KW-III handheld induction brazing system  Industry: Appliances & HVAC Materials: Steel hexagon (base 1’’/ 25.4 mm diameter; 0.1’’/ 2.54 mm wall thickness) A stainless steel pin (0.15’’/ 3.81 mm) Other Materials:  All-purpose black brazing flux Power: 1.43 kW Temperature: 1400 °F/ 760°C Time: 8 seconds Process: The two workpieces were carefully positioned together. All-purpose induction brazing black flux was added because it is ideal for high-temperature applications where rapid, localized heating is needed. The process of induction brazing was performed successfully within 8 seconds by using the  DW-UHF-6KW-III handheld induction brazing system, producing the induction heating power of 1.43 kW at 1400 °F/ 760°C.

induction brazing stainless steel to steel

High frequency magnetic induction brazing stainless steel to steel process

HLQ team was provided with 2 different parts to be brazed in our test laboratory. Objective: Induction Brazing of a 0.15’’/ 3.81mm stainless steel pin to a steel base. Equipment:  DW-UHF-6KW-III handheld induction brazing system  Industry: Appliances & HVAC Materials: Steel hexagon (base 1’’/ 25.4 mm diameter; 0.1’’/ 2.54 mm wall thickness) A stainless steel pin (0.15’’/ 3.81 mm) Other Materials:  All-purpose black brazing flux Power: 1.43 kW Temperature: 1400 °F/ 760°C Time: 8 seconds Process: The two workpieces were carefully positioned together. All-purpose induction brazing black flux was added because it is ideal for high-temperature applications where rapid, localized heating is needed. The process of induction brazing was performed successfully within 8 seconds by using the  DW-UHF-6KW-III handheld induction brazing system, producing the induction heating power of 1.43 kW at 1400 °F/ 760°C.

induction brazing stainless steel to steel

High frequency magnetic induction brazing stainless steel to steel process

HLQ team was provided with 2 different parts to be brazed in our test laboratory. Objective: Induction Brazing of a 0.15’’/ 3.81mm stainless steel pin to a steel base. Equipment:  DW-UHF-6KW-III handheld induction brazing system  Industry: Appliances & HVAC Materials: Steel hexagon (base 1’’/ 25.4 mm diameter; 0.1’’/ 2.54 mm wall thickness) A stainless steel pin (0.15’’/ 3.81 mm) Other Materials:  All-purpose black brazing flux Power: 1.43 kW Temperature: 1400 °F/ 760°C Time: 8 seconds Process: The two workpieces were carefully positioned together. All-purpose induction brazing black flux was added because it is ideal for high-temperature applications where rapid, localized heating is needed. The process of induction brazing was performed successfully within 8 seconds by using the  DW-UHF-6KW-III handheld induction brazing system, producing the induction heating power of 1.43 kW at 1400 °F/ 760°C.

induction brazing stainless steel to steel

High frequency magnetic induction brazing stainless steel to steel process

HLQ team was provided with 2 different parts to be brazed in our test laboratory. Objective: Induction Brazing of a 0.15’’/ 3.81mm stainless steel pin to a steel base. Equipment:  DW-UHF-6KW-III handheld induction brazing system  Industry: Appliances & HVAC Materials: Steel hexagon (base 1’’/ 25.4 mm diameter; 0.1’’/ 2.54 mm wall thickness) A stainless steel pin (0.15’’/ 3.81 mm) Other Materials:  All-purpose black brazing flux Power: 1.43 kW Temperature: 1400 °F/ 760°C Time: 8 seconds Process: The two workpieces were carefully positioned together. All-purpose induction brazing black flux was added because it is ideal for high-temperature applications where rapid, localized heating is needed. The process of induction brazing was performed successfully within 8 seconds by using the  DW-UHF-6KW-III handheld induction brazing system, producing the induction heating power of 1.43 kW at 1400 °F/ 760°C.

induction brazing stainless steel to steel

High frequency magnetic induction brazing stainless steel to steel process

HLQ team was provided with 2 different parts to be brazed in our test laboratory. Objective: Induction Brazing of a 0.15’’/ 3.81mm stainless steel pin to a steel base. Equipment:  DW-UHF-6KW-III handheld induction brazing system  Industry: Appliances & HVAC Materials: Steel hexagon (base 1’’/ 25.4 mm diameter; 0.1’’/ 2.54 mm wall thickness) A stainless steel pin (0.15’’/ 3.81 mm) Other Materials:  All-purpose black brazing flux Power: 1.43 kW Temperature: 1400 °F/ 760°C Time: 8 seconds Process: The two workpieces were carefully positioned together. All-purpose induction brazing black flux was added because it is ideal for high-temperature applications where rapid, localized heating is needed. The process of induction brazing was performed successfully within 8 seconds by using the  DW-UHF-6KW-III handheld induction brazing system, producing the induction heating power of 1.43 kW at 1400 °F/ 760°C.

induction brazing stainless steel to steel

High frequency magnetic induction brazing stainless steel to steel process

HLQ team was provided with 2 different parts to be brazed in our test laboratory. Objective: Induction Brazing of a 0.15’’/ 3.81mm stainless steel pin to a steel base. Equipment:  DW-UHF-6KW-III handheld induction brazing system  Industry: Appliances & HVAC Materials: Steel hexagon (base 1’’/ 25.4 mm diameter; 0.1’’/ 2.54 mm wall thickness) A stainless steel pin (0.15’’/ 3.81 mm) Other Materials:  All-purpose black brazing flux Power: 1.43 kW Temperature: 1400 °F/ 760°C Time: 8 seconds Process: The two workpieces were carefully positioned together. All-purpose induction brazing black flux was added because it is ideal for high-temperature applications where rapid, localized heating is needed. The process of induction brazing was performed successfully within 8 seconds by using the  DW-UHF-6KW-III handheld induction brazing system, producing the induction heating power of 1.43 kW at 1400 °F/ 760°C.

induction brazing stainless steel to steel

High frequency magnetic induction brazing stainless steel to steel process

HLQ team was provided with 2 different parts to be brazed in our test laboratory. Objective: Induction Brazing of a 0.15’’/ 3.81mm stainless steel pin to a steel base. Equipment:  DW-UHF-6KW-III handheld induction brazing system  Industry: Appliances & HVAC Materials: Steel hexagon (base 1’’/ 25.4 mm diameter; 0.1’’/ 2.54 mm wall thickness) A stainless steel pin (0.15’’/ 3.81 mm) Other Materials:  All-purpose black brazing flux Power: 1.43 kW Temperature: 1400 °F/ 760°C Time: 8 seconds Process: The two workpieces were carefully positioned together. All-purpose induction brazing black flux was added because it is ideal for high-temperature applications where rapid, localized heating is needed. The process of induction brazing was performed successfully within 8 seconds by using the  DW-UHF-6KW-III handheld induction brazing system, producing the induction heating power of 1.43 kW at 1400 °F/ 760°C.

induction brazing stainless steel to steel

High frequency magnetic induction brazing stainless steel to steel process

HLQ team was provided with 2 different parts to be brazed in our test laboratory. Objective: Induction Brazing of a 0.15’’/ 3.81mm stainless steel pin to a steel base. Equipment:  DW-UHF-6KW-III handheld induction brazing system  Industry: Appliances & HVAC Materials: Steel hexagon (base 1’’/ 25.4 mm diameter; 0.1’’/ 2.54 mm wall thickness) A stainless steel pin (0.15’’/ 3.81 mm) Other Materials:  All-purpose black brazing flux Power: 1.43 kW Temperature: 1400 °F/ 760°C Time: 8 seconds Process: The two workpieces were carefully positioned together. All-purpose induction brazing black flux was added because it is ideal for high-temperature applications where rapid, localized heating is needed. The process of induction brazing was performed successfully within 8 seconds by using the  DW-UHF-6KW-III handheld induction brazing system, producing the induction heating power of 1.43 kW at 1400 °F/ 760°C.