2022年11月18日星期五

High Speed Heating by Induction Heating System

One of the recent outstanding developments in the heat treating field has been the application of induction heating to localized surface hardening. The advances made contingent with the applica­tion of high frequency current have been nothing short of phenomenal. Starting a comparatively short time ago as a long-sought-after method of hardening bearing surfaces on crankshafts (sev­eral million of these are in use setting all time service records), today finds this very selective surfacing hardening method producing hardened areas on a multiplicity of parts. Yet, in spite of its present day breadth of application, induction hardening is still in its infant stage. Its probable utilization for the heat treating and hardening of metals, heating for forging or brazing, or solder­ing of similar and dissimilar metals, is unpre­dictable. Induction hardening results in the production of locally hardened steel objects with the desired degree of depth and hardness, essential metal­lurgical structure of core, demarcation zone, and hardened case, with a practical lack of distortion and no scale formation. It permits equipment de­sign which warrants mechanization of the whole operation to fulfill production line requirements. Time cycles of only a few seconds are maintained by automatic regulation of power and split second heating and quenching intervals indispensable to the creation of facsimile results of exacting special fixations. Induction hardening equipment permits the user to surface harden only the requisite por­tion of most any steel object and thus maintain the original ductility and strength; to harden articles of intricate design which cannot be feas­ibly treated in any other way; to eliminate usual expensive pretreatment such as copper plating and carburizing, and costly subsequent straight­ening and cleaning operations; to cut down on material cost by having a wide selection of steels from which to choose; and to harden a fully-ma­chined item without the necessity of any finishing operations. To the casual observer it would appear that in­duction hardening is possible as a result of some energy transformation occurring within an induc­tive region of copper. The copper carries an elec­trical current of high frequency and, within an interval of a few seconds, the surface of a piece of steel placed within this energized region is heated to its critical range and quenched to opti­mum hardness. To the manufacturer of equipment for this method of hardening it means the appli­cation of the phenomena of hysteresis, eddy cur­rents, and skin effect to the effective production of localized surface hardening. The heating is accomplished by use of high frequency currents. Specifically chosen frequencies from 2,000 to 10,000 cycles and upwards of 100,­000 cycles are being used extensively at the pres­ent time. Current of this nature in flowing through an inductor produces a high-frequency magnetic field within the region of the inductor. When a magnetic material such as steel is placed within this field, there is a dissipation of energy in the steel which produces heat. The molecules within the steel attempt to align themselves with the polarity of this field, and with this changing thousands of times per second, an enormous amount of internal molecular friction is developed as a result of the natural tendency for the steel to resist changes. In this manner the electrical energy is transformed, through the medium of friction, into heat. However, since another inherent characteristic of high frequency current is to concentrate on the surface of its conductor, only the surface layers become heated. This tendency, called “skin effect”, is a function of the frequency and, other things being equal, higher frequencies are effec­tive at shallower depths. The frictional action producing the heat is called hysteresis and is obviously dependent upon the magnetic qualities of the steel. Thus, when the temperature has passed the critical point at which the steel be­comes non-magnetic, all hysteretic heating ceases. There is an additional source of heat due to eddy currents which flow in the steel as a result of the rapidly changing flux in the field. With resistance of the steel increasing with tempera­ture, the intensity of this action is decreased as the steel becomes heated, and is only a fraction of its “cold” original value when the proper quenching temperature is reached. When the temperature of an inductively heated steel bar arrives at the critical point, heating due to eddy currents continues at a greatly reduced rate. Since the entire action goes on in the sur­face layers, only that portion is affected. The original core properties are maintained, the sur­face hardening being accomplished by quench­ing when complete carbide solution has been at­tained in the surface areas. Continued applica­tion of power causes an increase in depth of hardness, for as each layer of steel is brought to temperature, the current density shifts to the layer beneath which offers a lower resistance. It is obvious that the selection of the proper fre­quency, and control of power and heating time will make fulfillment of any desired specifica­tions of surface hardening possible. Metallurgy of Induction Heating The unusual behavior of steel when heated in­ductively and the results obtained merit a discus­sion of the metallurgy involved. Carbide solution rates of less than a second, higher hardness than that produced by furnace treatment, and a nodu­lar type of martensite are points of consideration that classify the metallurgy of induction harden­ing as “different”. Further, surface decarburiza­tion and grain growth do not occur because of the short heating cycle. Induction heating produces a hardness that is maintained through 80 percent of its depth, and from there on, a gradual decrease through a transition zone to the original hardness of the steel as found in the core which has not been affected. The bond is thus ideal, eliminating any chance of spalling or checking. Complete carbide solution and homogeneity as evidenced by maximum hardness can be accom­plished with a total heating time of 0.6 second. Of this time, only 0.2 to 0.3 second is actually above the lower critical. It is interesting to note that induction hardening equipment is in every day operation on a production basis with complete carbide solution, resulting from a heating and quenching cycle, the total time of which is less than 0.2 second. The fine nodular and more homogeneous mar­tensite which results from the induction harden­ing is more readily apparent with carbon steels than with alloy steel because of the nodular ap­pearance of most alloy martensite. This fine struc­ture must have for its origin an austenite which is the result of a more thorough carbide diffusion than is obtained with thermal heating. Practically instantaneous development of critical tempera­tures throughout the entire microstructure of the alpha iron and iron carbide is particularly con­ducive to rapid carbide solution and a distribution of constituents which has as its inevitable product a thoroughly homogeneous austentite. Further, the conversion of this structure to martensite will produce a martensite which possesses similar characteristics and a corresponding resistance to wear or penetrating instruments.

high speed heating by induction  

关注者

博客归档

我的简介

我的照片
HLQ induction heating machine manufacturer provides the service of induction brazing,melting,hot forming,hardening surface,annealing,shrink fitting,PWHT,etc.